| 引用本文: | 彭辰晨,邢洁芳,刘玉娇,季韩森,闫继芳,魏先福,黄蓓青.水性银墨基墨的粒径影响因素研究[J].包装工程,2020,41(11):145-150. |
| |
|
| |
|
|
| 本文已被：浏览 2276次 下载 1452次 |
码上扫一扫！ |
|
|
| 水性银墨基墨的粒径影响因素研究 |
|
彭辰晨1, 邢洁芳1, 刘玉娇1, 季韩森1, 闫继芳1, 魏先福2, 黄蓓青2
|
|
1.南京林业大学，南京 210037;2.北京印刷学院，北京 102600
|
|
| 摘要: |
| 目的 研究铝银浆的种类、研磨树脂的对应颜基比及分散剂配比对水性银墨基墨粒径的影响。 方法 以铝银浆为油墨颜料，与研磨树脂、分散剂、去离子水及助剂均匀混合搅拌，制备成水性银墨基墨，通过激光粒度仪测试基墨粒径。结果 使用DZR05号铝银浆，AZR研磨树脂，颜基比（质量比）为2∶3，760与3200分散剂的质量比为2∶3，分散剂的质量分数为5%时，制备的水性银墨基墨粒径最小。结论 性能良好的铝银浆，合适的研磨树脂及对应颜基比，适宜的分散剂配比及质量分数，有利于降低水性银墨基墨的粒径。 |
| 关键词: 水性银墨基墨 粒径 分散稳定性 单纯形重心试验法 |
| DOI：10.19554/j.cnki.1001-3563.2020.11.021 |
| 分类号:TS802.3 |
| 基金项目:江苏省产学研前瞻性联合研究项目（BY2016006-01） |
|
| Influencing Factors of Particle Size of Water-based Silver Ink Paste |
|
PENG Chen-chen1, XING Jie-fang1, LIU Yu-jiao1, JI HAN-sen1, YAN Ji-fang,1, WEI Xian-fu2, HUANG Bei-qing2
|
|
1.Nanjing Forestry University, Nanjing 210037, China;2.Beijing Institute of Graphic Communication, Beijing 102600, China
|
| Abstract: |
| The work aims to study the effects of the types of aluminum silver paste, the corresponding binder ratio of grinding resin, dispersant ratio and mass fraction of dispersants on the particle size of water-based silver ink paste. The water-based silver ink paste was prepared by mixing aluminum silver paste with grinding resin, dispersant, deionized water and auxiliary agent. The particle size of the ink paste was tested by laser particle size analyzer. The particle size of water-based silver ink paste prepared with DZR05 aluminum silver paste and AZR grinding resin was the smallest when the binder ratio was 2∶3, the ratio of 760 dispersant to 3200 dispersant was 2∶3 and the mass fraction of dispersant was 5%. The particle size of water-based silver ink paste can be reduced by aluminum silver paste with good properties, suitable grinding resin and its corresponding binder ratio, suitable dispersant ratio and mass fraction. |
| Key words: water-based silver ink paste particle size dispersion stability simple barycenter method |
|
|
|
|