| 摘要: |
| 分别以氧化淀粉、CMC和SAE类表面合成施胶剂为强化助剂，对瓦楞纸板进行了表面涂覆试验，研究了其边压强度变化情况；将上述施胶剂复配，以分散剂CMC用量、氧化淀粉与SAE混合溶液的质量分数、氧化淀粉与SAE配比、施胶温度为因素，应用正交试验法进行复配效果研究。试验结果表明，氧化淀粉、SAE和CMC的复配，比单独使用具有更好的增强效果。试验获得的最佳瓦楞纸板强化工艺参数是：CMC质量分数为5%，氧化淀粉与SAE混合溶液质量分数为9%，氧化淀粉与SAE质量比为1:10，施胶温度为85 ℃。 |
| 关键词: 瓦楞纸板 表面施胶 边压强度 正交试验 |
| DOI： |
| 分类号:TB484.1; TB487 |
| 基金项目: |
|
| Effect of Compound Surface Sizing Agent on Edgewise Compression Strength of Corrugated Paperboard |
|
HAO Xiao-meng, ZHANG Xin-chang
|
|
Jiangnan University, Wuxi 214122, China
|
| Abstract: |
| The edgewise compression strength of corrugated paperboard with oxidized starch, CMC, SAE synthesized surface sizing agent was studied. The effects of the amount of CMC, which was the dispersant, the mixed solution of oxidized starch and SAE, the proportion of oxidized starch and SAE, and the sizing temperature were investigated. The results showed that the combination of oxidized starch, CMC, SAE has better strengthening effect than used alone. The optimum technical strengthening conditions of corrugated board are 5%CMC, 9% mass fraction of mixed solution of oxidized starch and SAE, 1:10 mass ratio of oxidized starch and SAE, and sizing temperature 85 ℃. |
| Key words: corrugated paperboard surface sizing edgewise compression strength orthogonal experiment |